PA6-GF

Glass Fiber Reinforced PA6 (Nylon 6)

€65,10 EUR

Final price and VAT may change based on shipping destination at checkout.

Product Features
  • Built to Last
  • Dimensional Stability
  • Exceptional Thermal Properties
  • Chemical Resistance
  • Smooth Surface and More Colors
  • Diameter: 1.75mm +/- 0.03mm

Cautions for Use
  • 0.2 mm Nozzle Not Compatible
  • Stainless Steel Nozzle Not Recommended
  • AMS & AMS lite Compatible
  • Dry before Use

Type:
Size:
Color: Yellow (72400)
Quantity:
€65,10 EUR
Discover More Here!
The optimal nozzle for printing carbon fiber reinforced filaments!

Order Info
  • Order will be shipped out from DE warehouse in 1-3 business days once being processed.
  • Free Shipping over €55 (most EU countries)
  • Free Shipping over €119 (Norway, Cyprus, Malta, Switzerland)
  • Shipping rates vary by locations. See our Shipping Policy for details.


Bambu PA6-GF - Glass Fiber Reinforced Nylon

Bambu PA6-GF, also known as Nylon 6 with Glass Fiber, stands at the forefront of high-performance engineering plastics. Engineered to deliver exceptional strength, durability, dimensional stability. The PA6-GF is also more cost effective when compared to other top tier engineering filaments.

pa6-gf filament pa6-gf filament

Built to Last

Bambu PA6-GF is exceptionally strong and durable due to reinforced glass fibers, making it the perfect choice for prints that need to withstand heavy use and resist bending or breaking.

* Note: The printed part achieves better toughness after exposure to moisture.

petg translucent filament asa filament
petg translucent filament asa filament

Dimensional Stability

PA6-GF boasts unparalleled dimensional stability thanks to its glass fiber reinforcement, minimizing warping in comparison to standard PA filaments. Print with precise dimensions, even in the most intricate geometries.

petg translucent filament asa filament
petg translucent filament asa filament

Exceptional Thermal Properties

PA6-GF boasts a high heat deflection temperature and superior dimensional stability, enabling it to retain its mechanical properties even under elevated temperatures. This makes it ideal for demanding industrial and automotive applications.

pa6-gf filament pa6-gf filament

Filament Type PLA Basic ABS Normal PA PC PA6-GF PA6-CF PAHT-CF PET-CF
Heat Deflection Temperature / ℃ (0.45 MPa) 57 ℃ 87 ℃ 89 ℃ 117 ℃ 182 ℃ 186 ℃ 194 ℃ 205 ℃
rfid rfid

Chemical Resistance

PA6-GF offers excellent resistance to chemicals, oils, and many kinds of solvents, ensuring long-term performance in challenging environments.

petg translucent filament asa filament
petg translucent filament asa filament

Smooth Surface and More Colors

Bambu PA6-GF filaments are compatible with the Bambu AMS system, ready to print in multi-color. The special surface texture also blurs the layer lines, providing a smooth surface quality.

petg translucent filament asa filament
petg translucent filament asa filament


PA6-GF Hex Code Table

Color Hex Code Display
White #EAEAE4
Yellow #FFCE00
Lime #C5ED48
Blue #75AED8
Orange #FF4800
Brown #5B492F
Gray #353533
Black #000000


RFID for Intelligent Printing

All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).

Load and print! No more tedious setting steps.

rfid rfid

Parameters Comparison

Learn more different filaments comparison on Bambu Filament Guide >>

PA6-GF PA6-CF PAHT-CF
Composition PA6, glass fiber PA6, carbon fiber PA12 and other long-chain PA, carbon fiber
AMS Compatibility YES NO YES
Dry Out Before Use Required Required Required
Printing Speed < 130 mm/s < 100 mm/s < 100 mm/s
Printer Type Enclosure Enclosure Enclosure
Toughness (Impact Strength - XY, dry state) 27.2 kJ/m² 40.3 kJ/m² 57.5 kJ/m²
Toughness (Impact Strength - XY, wet state) 55.8 kJ/m² 57.2 kJ/m² 62.3 kJ/m²
Strength (Bending Strength - XY, dry state) 120 MPa 151 MPa 125 MPa
Strength (Bending Strength - XY, wet state) 71 MPa 95 MPa 115 MPa
Layer Strength (Bending Strength - Z, dry state) 51 MPa 80 MPa 61 MPa
Layer Strength (Bending Strength - Z, wet state) 33 MPa 45 MPa 49 MPa
Stiffness (Bending Modulus - XY, dry state) 3670 MPa 5460 MPa 4230 MPa
Stiffness (Bending Modulus - XY, wet state) 2120 MPa 3560 MPa 3640 MPa
Layer Adhesion (Impact Strength - Z, dry state) 4.1 kJ/m² 15.5 kJ/m² 13.3 kJ/m²
Heat Resistance(HDT, 0.45 MPa, Dry State) 182 ℃ 186 ℃ 194 ℃
Saturated Water Absorption Rate/%(25 °C, 55% RH) 2.56 2.35 0.88


Accessory Compatibility

Recommended Not Recommended
Build Plate Engineering Plate, High Temperature Plate or Textured PEI Plate Cool Plate
Hotend Hardened Steel 0.4mm / 0.6mm (recommended) / 0.8 mm Hotend with Stainless Steel Nozzle (all size)
Hotend with Hardened Steel Nozzle (0.2 mm)
Glue Bambu Glue Stick Bambu Liquid Glue
AMS & AMS lite AMS & AMS lite /

Recommended Printing Settings
Drying Settings before Printing 80 °C, 8 - 12 h
Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant)
Nozzle Temperature 260 - 290 °C
Bed Temperature (with Glue) 80 - 100 °C
Printing Speed < 130 mm/s
Physical Properties
Density 1.09 g/cm³
Vicat Softening Temperature 212 °C
Heat Deflection Temperature 186 °C
Melting Temperature 223 °C
Melt Index 6.8 ± 0.6 g/10 min
Mechanical Properties
Tensile Strength 102 ± 7 MPa
Breaking Elongation Rate 5.8 ± 1.6 %
Bending Modulus 5460 ± 280 MPa
Bending Strength 151 ± 8 MPa
Impact Strength 40.3 ± 2.5 kJ/m²



Printing Tips

• Bambu PA6-GF needs proper drying before printing: recommended drying temperature is 80 ℃ for 8 to 12 hours in a blast drying oven, or 90 to 100 ℃ for 10 to 12 hours on heat bed. (Do not exceed 100 ℃ because the spool may deform or even melt). For more details, please refer to: Printing tips for Engineering materials on WIKI.

• To prevent the filament from absorbing moisture, it is recommended to use an airtight storage container with desiccant during printing. For more details, please refer to: Printing tips for Engineering materials on WIKI.

• To minimize warping, avoid printing large-sized high infill density models. Use enclosed printers and ensure the build plate is properly applied with glue for better print adhesion before printing.

• For better print results and more details, please refer to: Printing tips for Engineering materials on WIKI.


Post-processing Tips

• We recommend removing the support structures within 2 hours after printing to prevent them from sticking after absorbing moisture. If sticking occurs, dry the model to ease the removal.

• Placing the printed part in a convection oven set between 80 to 130 degrees Celsius for 5 to 12 hours can further enhance the strength and rigidity of the print. Note: The effectiveness of this process depends on the structure, size, and conditions of the printed model. Some models may warp or deform after annealing. For more details, please refer to: Work after Printing Finished on WIKI.