PAHT-CF

Carbon Fiber Reinforced High Temperature Nylon

€43,99 EUR €53,99 EUR

Final price and VAT may change based on shipping destination at checkout.

Product Features

  • Low Moisture Absorption
  • Exceptional Mechanical Properties & Layer Adhesion
  • High Tensile Strength
  • Comes with High Temperature Reusable Spool
  • Diameter: 1.75mm +/- 0.03mm

Cautions for Use
  • 0.6 mm Nozzle Recommended
  • 0.2 mm Nozzle Not Compatible
  • Stainless Steel Nozzle Not Recommended
  • Dry before Use
  • AMS Compatible
  • Enclosure Printer Required

Note: PAHT-CF is an upgraded version of PA-CF (PA-CF was discontinued).

Type:
Size:
Color: Black (70100)
Quantity:
€43,99 EUR €53,99 EUR
Discover More Here!
The optimal nozzle for printing carbon fiber reinforced filaments!

Order Info
  • Order will be shipped out from DE warehouse in 1-3 business days once being processed.
  • Free Shipping over €55 (most EU countries)
  • Free Shipping over €119 (Norway, Cyprus, Malta, Switzerland)
  • Shipping rates vary by locations. See our Shipping Policy for details.

Bambu PAHT-CF

Bambu PAHT-CF is a composite of PA12 and carbon fiber. Inheriting the advantages of low water absorption from PA12 and high-performance carbon fiber, Bambu PAHT-CF offers excellent mechanical and thermal properties that can be maintained well even when the prints get wet. Higher Z adhesion layers and flexibility make it ideal for creating engineering parts such as functional prototypes, machining fixtures, injection molds, jigs, and low-volume production parts.

 

Low water absorption

With a 50% lower water absorption rate compared to normal PA-CF,

Bambu PAHT-CF maintains excellent mechanical properties and dimensional stability even when exposed to high humidity.


Deflection from Dry to Wet

paht-cf paht-cf


Mechanical Properties Comparison

Normal PA-CF PAHT-CF
Saturated Water Absorption Rate/% ( 25 °C, 55% RH ) 1.70 0.88
Bending Strength - XY/MPa (Dry) 128 125
Bending Strength - XY/MPa (Wet) 76 115
Bending Strength - Z/MPa (Dry) 48 61
Bending Strength - Z/MPa (Wet) 34 49
Bending Modulus - XY/MPa (Dry) 4420 4230
Bending Modulus - XY/MPa (Wet) 2210 3640
Bending Modulus - Z/MPa (Dry) 1470 1820
Bending Modulus - Z/MPa (Wet) 770 1480
Decline rate of mechanical properties after absorbing water/% 40%-45% 12%-18%

*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.

 

Exceptional Z-bonding

Bambu PAHT-CF shows much higher adhesion in Z layers compared to normal PA-CF,

bringing it the ability to withstand high levels of impact or stress without breaking or deforming.

paht-cf paht-cf

Z-layer Performance

Normal PA-CF PAHT-CF Improved %
Bending Strength - Z/MPa 48 61 27%
Bending Modulus - Z/MPa 1470 1820 24%
Impact Strength - Z/(kJ/m²) 5.7 13.3 133%

*Both PA-CF and PAHT-CF need to be dried at 80 °C for 12 hours before printing.


High tensile strength

Bambu PAHT-CF is designed to meet the demands of various industrial

and engineering applications where high strength and durability are required.

Designed for high-temperature resistance

The heat deflection temperature of Bambu PAHT-CF is up to 194℃ (0.45MPa)*, making it useful in applications where the printed parts may be exposed to high temperatures without deforming or losing their strength.