Bambu PLA Aero
Bambu PLA Aero achieves low density and light weight by foaming at high temperatures during printing and creating small holes inside the prints. It's the perfect choice for light-weight and energy-saving prints, including unmanned aerial vehicles (UAVs), aerodynamic models, and gliders.
Foaming PLA materials (PLA Aero) have high requirements for material drying and parameter settings. Please carefully read Instructions for printing aircraft model with foaming PLA (PLA Aero) before starting the printing process.
Low Density and Light Weight
Bambu PLA Aero has almost the same filament density as regular PLA, while the prints density is only 50% to 80%.
* When printing models of the same volume, PLA Aero is about half the weight of PLA Basic.
* When printing models of the same volume, PLA Aero is about half the weight of PLA Basic.
Controllable Model Density
Achieve lower density of the prints by increasing printing temperature and lowering flow rate.
* The average density of prints will vary with changes in parameters such as actual printing temperature, flow rate ratio, printing speed, model size, wall thickness and infill density.
| Parameter Setting | Average Density | |
| Printing Temperature | Increases ↗ | Decreases ↘ |
| Printing Speed | Increases ↗ | Stable or Increases ↗ |
| Flow Rate Ratio | Increases ↗ | Increases ↗ |
| Model Size | Increases ↗ | Decreases ↘ |
| Wall Thickness（Wall loops） | Increases ↗ | Increases ↗ |
| Infill Density | Increases ↗ | Increases ↗ |
The relationship between the maximum foaming rate, minimum print density, and printing temperature of PLA Aero.
|
Printing Temperature
|
Minimum Flow Rate Ratio
|
Maximum Volumetric Expansion Ratio
|
Maximum Foaming Rate
|
Minimum Prints Density
|
| 190 °C | ~ 0.95 | ~ 100% | ~ 0% | ~ 1.17 g/cm³ |
| 200 °C | 0.89 | 110% | 10% | 1.06 g/cm³ |
| 210 °C | 0.85 | 115% | 15% | 1.02 g/cm³ |
| 220 °C | 0.76 | 129% | 29% | 0.91 g/cm³ |
| 230 °C | 0.62 | 158% | 58% | 0.74 g/cm³ |
| 240 °C | 0.45 | 217% | 117% | 0.54 g/cm³ |
| 250 °C | 0.38 | 258% | 158% | 0.45 g/cm³ |
| 260 °C | 0.35 | 280% | 180% | 0.42 g/cm³ |
| 270 °C | 0.37 | 265% | 165% | 0.44 g/cm³ |
Specimen Test: Nozzle Type: 0.4 mm; Printing Speed: 80 mm/s; Model size (L*W*H): 80*10*4 mm³ (the XY direction)
The actual required flow rate ratio and final model density may vary with different models.
Tough with Good Impact Resistance
Compared to pre-foaming Wood PLA, Bambu PLA Aero and its prints are tougher and more resistant to impact, collision, and falling.
Matte Finish For Easy Coloring
Bambu PLA Aero provides an easy-to-color matte surface texture with better dyeing results as compared to PLA Basic.
Parameters Comparison
Learn more different filaments comparison on Bambu Filament Guide >>
| PLA Basic | PLA Aero | |
| Printing Temperature | 190 - 230 ℃ | 220 - 260 ℃ |
| Printing Speed | < 300 mm/s | < 180 mm/s |
| Flow Rate Ratio | 0.96 - 1 | 0.5 - 0.8 |
| Filament Density | 1.24 g/cm³ | 1.21 g/cm³ |
| Foaming Rate | / | 0 - 120% |
| Prints Density | 1.21 g/cm³ | 0.55 - 1.05 g/cm³ |
Accessory Compatibility
| Recommended | Not Recommended | |
| Build Plate | Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate | / |
| Hotend | Hotend with Hardened Steel Nozzle 0.4 mm Hotend with Stainless Steel Nozzle 0.4 mm |
Hotend with Hardened Steel Nozzle 0.6 mm / 0.8 mm Hotend with Stainless Steel Nozzle 0.2 mm |
| Glue | Bambu Liquid Glue Glue Stick |
/ |
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 55 °C，8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 220 - 260 °C |
| Bed Temperature (with Glue) | 35 - 45 °C |
| Printing Speed | < 180 mm/s |
| Physical Properties | |
| Density | 1.21 g/cm³ |
| Vicat Softening Temperature | 54 °C |
| Heat Deflection Temperature | 53 °C |
| Melting Temperature | 153 °C |
| Melt Index | 7.7 ± 0.6 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 24 ± 2 MPa |
| Breaking Elongation Rate | 2.6 ± 0.7 % |
| Bending Modulus | 1690 ± 120 MPa |
| Bending Strength | 45 ± 4 MPa |
| Impact Strength | 28.8 ± 1.3 kJ/m² |
Printing Tips
• PLA Aero filament is relatively soft which may result in material loading and unloading failures during AMS printing.
• Drying conditions: 55℃ for 8 hrs. PLA Aero is highly sensitive to humidity. To achieve optimal printing performance, it is recommeded further drying before use and after storage. For more details please refer to: Filament drying instructions on WIKI.